Frame Head Production Process In Category 3 Frame Chassis At Pt. Prime Dual Core
Abstract
The frame is the main component of the chassis that functions to withstand shock, pressure and vibration when operating on the road. The chassis frame is made of SS400 material which has a good level of strength to withstand static loads, the Frame Chassis formation process uses a cold working process. This writing aims to determine the production process of the Frame Head on the Frame Chassis category 3 as well as knowing the machines used in the Frame Head production process and knowing the total tonnage required for the 400 ton Stamping machine in the blanking and piercing process on the Crossmember 0101 part, from observations that have been made. it was done that to carry out the Frame Head production process on Frame Chassis category 3, through the process of forming material or forming with the blanking, piercing, and bending methods using a 300 ton to 500 ton stamping machine, then continued with the unification process using a GMAW welding machine ( Gas Metal Arc Welding), then continued with the painting process using powder coating with the dipping method for 2 minutes, and in the Crossmember 0101 forming part process using a 400 ton Stamping machine, the total tonnage of the blanking and piercing cutting force was obtained on the Crossmember 0101 part (added with backup/strippin style g force) is 470.069 Tons.
Downloads
References
Abubakar, M., Krisnowo, A., Suryaputra, H., & Noviantoro, B. (2017). Design dan Analisis Statik Rangka Chassis Square Bar dengan FEM. Mesin, 26(2), 102-111.
China Brill Special Steel. SPH440 OD Specification of Material.
Faisyal, Y. (2002). Perencanaan Proses Produksi Packing Silinder Head Honda GL 200 Dengan Proses Blanking.
Susanto, S. (2017). Modifikasi Profressive Tool Plat Penyangga Baut Gear Belakang Pada Sepeda Motor Yamaha Jupiter Kapasitas 300 Buah/Jam. Jurnal Teknik Mesin, 7(02).
Ardhayananta, Hosta. dkk. Pengaruh Pengerjaan Dingin Terhadap Ketahanan Korosi Lapisan Hasil Hot Dip Galvanizing AISI 1020 di Media NaCl. Surabaya: Institut Teknologi Sepuluh Nopember Surabaya.
Eriko, S. (2014). Modifikasi Dies Dengan Variasi Radius Fillet Untuk Meminimalisir Die Fill Defect Pada Produk Metal Gasket (Doctoral dissertation, Universitas Brawijaya).
Saputra Utama, R. I. Z. K. I. (2019). Modifikasi Las GTAW Semi Otomatis Dengan Penambahan Feeder Las GMAW (Doctoral dissertation, Vokasi undip).
Miranda, Y., & Made, A. M. (2020). Analisa Perbedaan Temperatur Pada Material Baja Karbon Rendah S355JO Terhadap Distorsi Pada Pengelasan SMAW. Zona Mesin: Program Studi Teknik Mesin Universitas Batam, 9(1).
Novianto, N. D. (2015). Penggunaan Alat Pelindung Diri (APD) Pada Pekerja Pengecoran Logam PT. Sinar Semesta (Studi Kasus Tentang Perilaku Penggunaan Alat Pelindung Diri (APD) Ditinjau Dari Pengetahuan Terhadap Potensi Bahaya Dan Resiko Kecelakaan Kerja Pada Pekerja Pengecoran L. Jurnal Kesehatan Masyarakat (e-Journal), 3(1), 417-428.
Nastiti, H. (2014). Analisis Pengendalian Kualitas Produk Dengan Metode Statistical Quality Control (Studi Kasus: pada PT “X” Depok). Sustainable Competitive Advantage (SCA), 4(1).